SiCf/Ti65复合材料界面反应与基体相变机理
王超1,2, 张旭1(
), 王玉敏1(), 杨青1, 杨丽娜1, 张国兴1, 吴颖1, 孔旭1, 杨锐1
), 王玉敏1(), 杨青1, 杨丽娜1, 张国兴1, 吴颖1, 孔旭1, 杨锐1
Mechanisms of Interfacial Reaction and Matrix Phase Transition in SiCf /Ti65 Composites
WANG Chao1,2, ZHANG Xu1(), WANG Yumin1(), YANG Qing1, YANG Lina1, ZHANG Guoxing1, WU Ying1, KONG Xu1, YANG Rui1
), WANG Yumin1(), YANG Qing1, YANG Lina1, ZHANG Guoxing1, WU Ying1, KONG Xu1, YANG Rui1
图10. SiCf /Ti65 复合材料在不同状态下的物相分布和元素扩散路径示意图
Color online
(a) precursor wire
(b) as-processed stage
(c) early stage of thermal exposure
(d) late stage of thermal exposure
Fig.10. Schematics of distributions of interfacial reaction products and element diffusion paths (shown by arrows) for SiCf /Ti65 composites