激光工艺参数对TiC增强钴基合金激光熔覆层组织及性能的影响
童文辉(
), 张新元, 李为轩, 刘玉坤, 李岩, 国旭明
), 张新元, 李为轩, 刘玉坤, 李岩, 国旭明
Effect of Laser Process Parameters on the Microstructure and Properties of TiC Reinforced Co-Based Alloy Laser Cladding Layer
TONG Wenhui(), ZHANG Xinyuan, LI Weixuan, LIU Yukun, LI Yan, GUO Xuming
), ZHANG Xinyuan, LI Weixuan, LIU Yukun, LI Yan, GUO Xuming
图8. 激光扫描速率为410 mm/min、不同激光功率条件下制备得到的熔覆层横截面SEM像及EDS结果
(a, b) P=3.6 kW；(c, d) P=3.4 kW；(e, f) P=3.2 kW
Fig.8. SEM images (a, c, e) and corresponding EDS results (b, d, f) of the cross-sections of cladding layers (V=410 mm/min)