激光工艺参数对TiC增强钴基合金激光熔覆层组织及性能的影响
童文辉(
), 张新元, 李为轩, 刘玉坤, 李岩, 国旭明
), 张新元, 李为轩, 刘玉坤, 李岩, 国旭明
Effect of Laser Process Parameters on the Microstructure and Properties of TiC Reinforced Co-Based Alloy Laser Cladding Layer
TONG Wenhui(), ZHANG Xinyuan, LI Weixuan, LIU Yukun, LI Yan, GUO Xuming
), ZHANG Xinyuan, LI Weixuan, LIU Yukun, LI Yan, GUO Xuming
图3. 激光扫描速率390 mm/min、不同激光功率下熔覆层组织
(a) P=3.2 kW；(b) P=3.3 kW；(c) P=3.4 kW；(d) P=3.5 kW；(e) P=3.6 kW
Fig.3. Microstructures of cladding layer of different laser powers at V=390 mm/min