固溶温度对Fe-19Mn合金的γ→ε相变和阻尼性能的影响
王世宏, 李健(
), 柴锋, 罗小兵, 杨才福, 苏航
), 柴锋, 罗小兵, 杨才福, 苏航
Influence of Solution Temperature on γ→ε Transformation and Damping Capacity of Fe-19Mn Alloy
WANG Shihong, LI Jian(), CHAI Feng, LUO Xiaobing, YANG Caifu, SU Hang
), CHAI Feng, LUO Xiaobing, YANG Caifu, SU Hang
图8. 950 ℃固溶处理试样的ε-马氏体中层错的双束明场像
Fig.8. Bright-field TEM images of stacking faults in ε-martensite with different plate thickness under two-beam condition (a~c), and corresponding SAED patterns for ε-martensite in Fig.7a (d), and for ε-martensite in Figs.7b and c (e),respectively