固溶温度对Fe-19Mn合金的γ→ε相变和阻尼性能的影响
王世宏, 李健(
), 柴锋, 罗小兵, 杨才福, 苏航
), 柴锋, 罗小兵, 杨才福, 苏航
Influence of Solution Temperature on γ→ε Transformation and Damping Capacity of Fe-19Mn Alloy
WANG Shihong, LI Jian(), CHAI Feng, LUO Xiaobing, YANG Caifu, SU Hang
), CHAI Feng, LUO Xiaobing, YANG Caifu, SU Hang
图7. γ-奥氏体中层错在双束条件下的TEM像及SAED谱
Fig.7. Bright-field (a, d) and dark-field (b, e) TEM images of stacking faults in γ-austenite of 950 ℃ (a, b) and 1050 ℃ (d, e) solution treated sample under two-beam condition, and corresponding SAED patterns for circle areas A (c) and B (f) in Figs.7a and d, respectively