固溶温度对Fe-19Mn合金的γ→ε相变和阻尼性能的影响
王世宏, 李健(
), 柴锋, 罗小兵, 杨才福, 苏航
), 柴锋, 罗小兵, 杨才福, 苏航
Influence of Solution Temperature on γ→ε Transformation and Damping Capacity of Fe-19Mn Alloy
WANG Shihong, LI Jian(), CHAI Feng, LUO Xiaobing, YANG Caifu, SU Hang
), CHAI Feng, LUO Xiaobing, YANG Caifu, SU Hang
图6. 1100 ℃固溶处理试样的TEM像和选区电子衍射(SAED)谱
Fig.6. Bright-field TEM image of γ-austenite and ε-martensite (a), dark-field images of γ-austenite (b) and ε-martensite (c) of 1100 ℃ solution treated sample, and corresponding selected area electron diffraction (SAED) patterns for areas A~C in Fig.6a (d~f)