Ti-6Al-4V合金β→α相变中晶界α相形成机制的相场模拟
孙佳1,2, 李学雄1, 张金虎1, 王刚3, 杨梅4, 王皞1,5, 徐东生1,5(
)
)
Phase Field Modeling of Formation Mechanism of Grain Boundary Allotriomorph in β→α Phase Transformation in Ti-6Al-4V Alloy
SUN Jia1,2, LI Xuexiong1, ZHANG Jinhu1, WANG Gang3, YANG Mei4, WANG Hao1,5, XU Dongsheng1,5()
)
图5. 不连续αGB的形成过程：ξnoise=0.05、tnoise=50 s条件下的模拟组织局部放大图
Fig.5. Local zoomed-in view of microstructures of incontinuous αGB under the condition ξnoise=0.05 and tnoise=50 s at t=55 s (a), t=60 s (b), t=65 s (c), t=70 s (d), t=75 s (e) and t=80 s (f)