Orientation Selection Behavior During Secondary Recrystallization in Grain-Oriented Silicon Steel
XU Zhanyi1, SHA Yuhui1(), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
图7. 不同抑制力水平下经1000 ℃保温100 s后二次再结晶晶粒尺寸等值线图
Fig.7. Grain size contours with variables of emj and initial grain size under Z=0.071 μm-1 (a) and Z=0.1 μm-1 (b) after annealing at 1000 ℃ for 100 s