取向硅钢二次再结晶过程中的取向选择行为
许占一1, 沙玉辉1(
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
Orientation Selection Behavior During Secondary Recrystallization in Grain-Oriented Silicon Steel
XU Zhanyi1, SHA Yuhui1(), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
图6. 经1000 ℃保温不同时间后二次再结晶晶粒尺寸等值线
Fig.6. Grain size contours with variables of emj and initial grain size at the beginning of secondary recrystallization after annealing at 1000 ℃ for 100 s (a) and 200 s (b) (emj—relative grain boundary energy coefficient, Z—Zener factor, t—annealing time, sold line—grain size contour, dash line—critical condition of secondary recrystallization)