取向硅钢二次再结晶过程中的取向选择行为
许占一1, 沙玉辉1(
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
Orientation Selection Behavior During Secondary Recrystallization in Grain-Oriented Silicon Steel
XU Zhanyi1, SHA Yuhui1(), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
图3. 慢升温至1000 ℃保温100和200 s后Fe-3.25%Si取向硅钢的组织及二次再结晶晶粒取向