取向硅钢二次再结晶过程中的取向选择行为
许占一1, 沙玉辉1(
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
Orientation Selection Behavior During Secondary Recrystallization in Grain-Oriented Silicon Steel
XU Zhanyi1, SHA Yuhui1(), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
图2. Fe-3.25%Si取向硅钢初次再结晶织构及Goss晶粒取向偏差角分布
Fig.2. φ2=45° section of ODF (levels: 1, 2, 3?) (a), number fraction of several main texture components (b) and deviation angle distribution of Goss grains (c) in primarily recrystallized Fe-3.25%Si grain-oriented silicon steel (ODF—orientation distribution function; φ1, φ2, Φ—Euler angles)
Color online