取向硅钢二次再结晶过程中的取向选择行为
许占一1, 沙玉辉1(
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
), 张芳1, 章华兵2, 李国保2, 储双杰2, 左良1,3
Orientation Selection Behavior During Secondary Recrystallization in Grain-Oriented Silicon Steel
XU Zhanyi1, SHA Yuhui1(), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
), ZHANG Fang1, ZHANG Huabing2, LI Guobao2, CHU Shuangjie2, ZUO Liang1,3
图1. 初次再结晶后与二次再结晶开始时Fe-3.25%Si取向硅钢中基体和Goss晶粒尺寸分布
Fig.1. Grain size distributions of matrix and Goss grains in Fe-3.25%Si grain-oriented silicon steel after primary recrystallization (a) and at the beginning of secondary recrystallization (b)