Low-Cycle Fatigue Behavior of 1100 MPa Grade High-Strength Steel
ZHOU Hongwei1,2, BAI Fengmei3,4(), YANG Lei1,2, CHEN Yan1,2, FANG Junfei1,2, ZHANG Liqiang3, YI Hailong4, HE Yizhu1,2
), YANG Lei1,2, CHEN Yan1,2, FANG Junfei1,2, ZHANG Liqiang3, YI Hailong4, HE Yizhu1,2
图7. 不同应变幅下高强钢疲劳裂纹于试样表面萌生
Fig.7. Fatigue cracks initiated from the surface of specimens under the strain amplitudes of 0.4% (a), 0.6% (b), 0.8% (c) and 1.2% (d)