1100 MPa级高强钢的低周疲劳行为
|
周红伟 1,2, 白凤梅 3,4( ), 杨磊 1,2, 陈艳 1,2, 方俊飞 1,2, 张立强 3, 衣海龙 4, 何宜柱 1,2
|
Low-Cycle Fatigue Behavior of 1100 MPa Grade High-Strength Steel
|
ZHOU Hongwei 1,2, BAI Fengmei 3,4( ), YANG Lei 1,2, CHEN Yan 1,2, FANG Junfei 1,2, ZHANG Liqiang 3, YI Hailong 4, HE Yizhu 1,2
|
|
图6. 高强钢在应变幅为0.4%和1.0%下疲劳断裂试样的TEM像
|
Fig.6. TEM images of fatigue fracture specimens (a, b) lath structure under the strain amplitude of 0.4% at low (a) and high (b) magnifications (c) low dislocation density, precipitate, PAGB, lath under the strain amplitude of 1.0% (d) crack propagation path indicated by arrows under the strain amplitude of 1.0%
|
|
|
|
|