1100 MPa级高强钢的低周疲劳行为
|
周红伟 1,2, 白凤梅 3,4( ), 杨磊 1,2, 陈艳 1,2, 方俊飞 1,2, 张立强 3, 衣海龙 4, 何宜柱 1,2
|
Low-Cycle Fatigue Behavior of 1100 MPa Grade High-Strength Steel
|
ZHOU Hongwei 1,2, BAI Fengmei 3,4( ), YANG Lei 1,2, CHEN Yan 1,2, FANG Junfei 1,2, ZHANG Liqiang 3, YI Hailong 4, HE Yizhu 1,2
|
|
图5. 高强钢中碳化物强化相形貌、SAED花样及EDS分析
|
Fig.5. TEM images, SAED pattern and EDS analyses of high-strength steel (a) spherical precipitate (Inset is the SAED pattern of the carbide) (b) short rod-shaped precipitate (c, d) EDS of precipitates denoted by cycles in Figs.5a (c) and b (d), respectively
|
|
|
|
|