Formation and Friction Properties of Electron Beam Cladding (Ti, W)C1-x Composite Coatings on Ti-6Al-4V

LIU Donglei, CHEN Qing, WANG De, ZHANG Rui, Tomiko Yamaguchi, WANG Wenqin

表2 图9中不同点的元素EDS成分分析 (atomic fraction / %)

Table 2 EDS analyses of elements at different points in Fig.9

Point C O Al Ti Fe Co W 1 0 42.28 6.42 49.47 1.83 0 0 2 2.57 47.16 4.03 25.57 19.64 0.35 0.67 3 5.02 41.33 5.43 42.92 4.45 0.26 0.58 4 1.25 46.98 5.56 42.89 2.04 0.38 0.89