Ti-6Al-4V表面电子束熔覆(Ti, W)C1-x复合涂层的形成及摩擦性能
刘东雷1, 陈情1, 王德2, 张睿2, 王文琴1,4(
)
)
Formation and Friction Properties of Electron Beam Cladding (Ti, W)C1-x Composite Coatings on Ti-6Al-4V
LIU Donglei1, CHEN Qing1, WANG De2, ZHANG Rui2, Tomiko Yamaguchi3, WANG Wenqin1,4()
)
图3. 不同熔覆电流时，涂层不同部位显微组织的SEM-BSE像(从左到右分别为上部、中部和界面处）
Fig.3. SEM-BSE images of different parts of the coating (upper, middle and interface from left to right) under different cladding currents
(a~c) 12 mA (d~f) 15 mA (g~i) 18 mA