Mg-5.6Gd-0.8Zn合金多向锻造过程中的变形机制及动态再结晶
张阳, 邵建波, 陈韬, 刘楚明, 陈志永()
Deformation Mechanism and Dynamic Recrystallization of Mg-5.6Gd-0.8Zn Alloy During Multi-Directional Forging
ZHANG Yang, SHAO Jianbo, CHEN Tao, LIU Chuming, CHEN Zhiyong()

图10. 合金2道次锻造后同一晶粒内的孪生及扭折现象分析

Fig.10. Analyses of twinned and kinked grains of the alloy in 2-pass
Color online
(a) orientation map of twinned and kinked grains
(b) misorientation angle distribution
(c) orientation coloring map of kink region (Fig.10c hides the twined region of Fig.10a)
(d) in-grain misorientation axes (IGMA) distribution ("pts" is the abbreviation of "points", and means the number of points with the defined misorientation
(e) magnified view of black-lined region in Fig.10a
(f) {0001}, {10ˉ10} and {11ˉ20} pole figures of grain in Fig.10e (Numbers 1~3 represent the matrix, kinked region and twined region respectively; the arrow in {10ˉ10} pole figure means one of the {10ˉ10} pole of the kink band and the matrix is coincided; the arrow in {11ˉ20} pole figure means one of the {11ˉ20} pole of the twin and the matrix is coincided)