冷变形和固溶温度对HR3C钢中σ相析出行为的影响
|
曹铁山 1,2, 赵津艺 1, 程从前 1, 孟宪明 3, 赵杰 1( )
|
Effect of Cold Deformation and Solid Solution Temperature on σ-phase Precipitation Behavior in HR3C Heat Resistant Steel
|
CAO Tieshan 1,2, ZHAO Jinyi 1, CHENG Congqian 1, MENG Xianming 3, ZHAO Jie 1( )
|
|
图4. 冷变形8%的HR3C钢经不同固溶温度处理后750 ℃长时间时效显微组织的OM像
|
Fig.4. OM images of microstructues of HR3C steel with 8% cold-deformation after different solution treatments and ageing at 750 ℃ for different time (a) 1143 ℃ solution and ageing 1500 h (b) 1143 ℃ solution and ageing 2000 h (c) 1193 ℃ solution and ageing 1500 h (d) 1193 ℃ solution and ageing 3000 h
|
|
|
|
|