冷变形和固溶温度对HR3C钢中σ相析出行为的影响
曹铁山1,2, 赵津艺1, 程从前1, 孟宪明3, 赵杰1(
)
)
Effect of Cold Deformation and Solid Solution Temperature on σ-phase Precipitation Behavior in HR3C Heat Resistant Steel
CAO Tieshan1,2, ZHAO Jinyi1, CHENG Congqian1, MENG Xianming3, ZHAO Jie1()
)
图2. 冷变形8%的HR3C钢在不同温度固溶处理后的显微组织的OM像
Fig.2. OM images of microstructures of 8% cold-deformed HR3C steel after solution treated at 1093 ℃ (a), 1143 ℃ (b) and 1193 ℃ (c)