高钛耐磨钢中TiC析出行为及其对耐磨粒磨损性能的影响
孙新军(),刘罗锦,梁小凯,许帅,雍岐龙
TiC Precipitation Behavior and Its Effect on Abrasion Resistance of High Titanium Wear-Resistant Steel
SUN Xinjun(),LIU Luojin,LIANG Xiaokai,XU Shuai,YONG Qilong

图14. Ti60钢经不同温度固溶处理后TiC粒子粒度分布(0~300 nm)

Fig.14. TiC particle size distribution (0~300 nm) of Ti60 steel subjected to solution treatments at different temperatures