高钛耐磨钢中TiC析出行为及其对耐磨粒磨损性能的影响
孙新军(),刘罗锦,梁小凯,许帅,雍岐龙
TiC Precipitation Behavior and Its Effect on Abrasion Resistance of High Titanium Wear-Resistant Steel
SUN Xinjun(),LIU Luojin,LIANG Xiaokai,XU Shuai,YONG Qilong

图13. Ti60钢900 ℃淬火态及随后经过1200和1350 ℃固溶处理后TiC粒子形貌的SEM和TEM像

Fig.13. SEM (a~c) and TEM (d~f) images of TiC particles of Ti60 steel quenched at 900 ℃ (a, d) and subsequently subjected to solution treatment at 1200 ℃ (b, e) and 1350 ℃ (c, f)