高强度含N节Ni奥氏体不锈钢08Cr19Mn6Ni3Cu2N (QN1803)的显微组织及性能
蒋一1,程满浪2,姜海洪1,周庆龙1,姜美雪1,江来珠1(
),蒋益明2
),蒋益明2
Microstructure and Properties of 08Cr19Mn6Ni3Cu2N (QN1803) High Strength Nitrogen Alloyed LowNickel Austenitic Stainless Steel
JIANG Yi1,CHENG Manlang2,JIANG Haihong1,ZHOU Qinglong1,JIANG Meixue1,JIANG Laizhu1(),JIANG Yiming2
),JIANG Yiming2
图17. 拉深制品在0.16%HCl+6%FeCl3溶液浸泡24 h后宏观形貌
Fig.17. Macrostructures of deep drawing products with height 40 mm and diameter 50 mm immersed in 0.16%HCl+6%FeCl3 solution for 24 h