钢的高性能化理论与技术进展
董瀚1,2(
),廉心桐1,胡春东1,陆恒昌1,彭伟1,赵洪山1,徐德祥1
),廉心桐1,胡春东1,陆恒昌1,彭伟1,赵洪山1,徐德祥1
High Performance Steels: the Scenario of Theoryand Technology
DONG Han1,2(),LIAN Xintong1,HU Chundong1,LU Hengchang1,PENG Wei1,ZHAO Hongshan1,XU Dexiang1
),LIAN Xintong1,HU Chundong1,LU Hengchang1,PENG Wei1,ZHAO Hongshan1,XU Dexiang1
图10. A286样品显微组织及A286样品与进口产品在650 ℃持久实验后的性能对比
Fig.10. Microstructure of A286 sample (a) and comparisons of mechanical property between A286 sample and imported A286 product after rupture test of 385 MPa and 100 h at 650 ℃ (b)