CoCrFeNiMo0.2高熵合金的不完全再结晶组织与力学性能
|
曹育菡 1,王理林 2,吴庆峰 2,何峰 2( ),张忠明 1,王志军 2
|
Partially Recrystallized Structure and Mechanical Properties of CoCrFeNiMo0.2 High-Entropy Alloy
|
CAO Yuhan 1,WANG Lilin 2,WU Qingfeng 2,HE Feng 2( ),ZHANG Zhongming 1,WANG Zhijun 2
|
|
图6. CoCrFeNiMo0.2高熵合金RTR35%和CTR35%试样经800 ℃、30 min退火处理后显微组织的SEM像
|
Fig.6. Low (a, c) and high (b, d) magnified SEM images of CoCrFeNiMo0.2 high-entropy alloy samples of RTR35%+800 ℃, 30 min (a, b) and CTR35%+800 ℃, 30 min (c, d) |
|
|
|
|