CoCrFeNiMo0.2高熵合金的不完全再结晶组织与力学性能
曹育菡1,王理林2,吴庆峰2,何峰2(
),张忠明1,王志军2
),张忠明1,王志军2
Partially Recrystallized Structure and Mechanical Properties of CoCrFeNiMo0.2 High-Entropy Alloy
CAO Yuhan1,WANG Lilin2,WU Qingfeng2,HE Feng2(),ZHANG Zhongming1,WANG Zhijun2
),ZHANG Zhongming1,WANG Zhijun2
图4. CoCrFeNiMo0.2高熵合金RTR35%和CTR35%试样经800 ℃、30 min退火处理后的EBSD像
Fig.4. Inverse pole figures (IPFs) (a, c) and Kernel average misorientations (KAMs) (b, d) images of the CoCrFeNiMo0.2 high-entropy alloy samples of RTR35%+800 ℃, 30 min (a, b) and CTR35%+800 ℃, 30 min (c, d)Color online