CoCrFeNiMo0.2高熵合金的不完全再结晶组织与力学性能
|
曹育菡 1,王理林 2,吴庆峰 2,何峰 2( ),张忠明 1,王志军 2
|
Partially Recrystallized Structure and Mechanical Properties of CoCrFeNiMo0.2 High-Entropy Alloy
|
CAO Yuhan 1,WANG Lilin 2,WU Qingfeng 2,HE Feng 2( ),ZHANG Zhongming 1,WANG Zhijun 2
|
|
图3. CoCrFeNiMo0.2高熵合金RTR35%和CTR35%试样及其经800 ℃、30 min退火处理后显微组织的OM像
|
Fig.3. OM images of the CoCrFeNiMo0.2 high-entropy alloy samples of RTR35% (a), CTR35% (b), RTR35%+800 ℃, 30 min (c) and CTR35%+800 ℃, 30 min (d) |
|
|
|
|