γ/ε双相Fe-19Mn合金在拉伸变形过程中的组织演变和加工硬化行为
王世宏1,李健1(
),葛昕1,2,柴锋1,罗小兵1,杨才福1,苏航1
),葛昕1,2,柴锋1,罗小兵1,杨才福1,苏航1
Microstructural Evolution and Work Hardening Behavior of Fe-19Mn Alloy Containing Duplex Austenite and ε-Martensite
WANG Shihong1,LI Jian1(),GE Xin1,2,CHAI Feng1,LUO Xiaobing1,YANG Caifu1,SU Hang1
),GE Xin1,2,CHAI Feng1,LUO Xiaobing1,YANG Caifu1,SU Hang1
图8. 不同变形量试样的XRD谱及各相含量随变形量的变化趋势
Fig.8. XRD spectra (a, b) and phase fractions (c) of samples with different tensile deformations (Fig.8b shows the XRD spectra between 46°~54° in Fig.8a)