Zr-0.75Sn-0.35Fe-0.15Cr合金在250 ℃去离子水中的初期腐蚀行为
姚美意1,2(
),张兴旺1,2,侯可可1,2,张金龙1,2,胡鹏飞1,2,彭剑超1,2,周邦新1,2
),张兴旺1,2,侯可可1,2,张金龙1,2,胡鹏飞1,2,彭剑超1,2,周邦新1,2
The Initial Corrosion Behavior of Zr-0.75Sn-0.35Fe-0.15Cr Alloy in Deionized Water at 250 ℃
YAO Meiyi1,2(),ZHANG Xingwang1,2,HOU Keke1,2,ZHANG Jinlong1,2,HU Pengfei1,2,PENG Jianchao1,2,ZHOU Bangxin1,2
),ZHANG Xingwang1,2,HOU Keke1,2,ZHANG Jinlong1,2,HU Pengfei1,2,PENG Jianchao1,2,ZHOU Bangxin1,2
图6. Zr/O比为3.10处(图2f中点6)的TEM像和超结构SAED花样
Fig.6. TEM image (a) and SAED patterns of superstructure (b, c) formed at a Zr/O ratio of 3.10 (point 6 in Fig.2f)