W含量对一种高W镍基高温合金显微组织的影响
华涵钰1,2,谢君1(
),舒德龙1,侯桂臣1,盛乃成1,于金江1,崔传勇1,孙晓峰1,周亦胄1
),舒德龙1,侯桂臣1,盛乃成1,于金江1,崔传勇1,孙晓峰1,周亦胄1
Influence of W Content on the Microstructure of Nickel Base Superalloy with High W Content
HUA Hanyu1,2,XIE Jun1(),SHU Delong1,HOU Guichen1,Naicheng SHENG1,YU Jinjiang1,CUI Chuanyong1,SUN Xiaofeng1,ZHOU Yizhou1
),SHU Delong1,HOU Guichen1,Naicheng SHENG1,YU Jinjiang1,CUI Chuanyong1,SUN Xiaofeng1,ZHOU Yizhou1
图8. 16%W镍基高温合金中α-W相形貌的SEM-SE和SEM-BSE像
Fig.8. SEM-SE (a) and SEM-BSE (b) images of α-W in the nickel base superalloy containing 16%W