Mechanism of TiN Fracture During the Tensile Process of NM500 Wear-Resistant Steel
WU Xiang,ZUO Xiurong(),ZHAO Weiwei,WANG Zhongyang
),ZHAO Weiwei,WANG Zhongyang
图8. NM500钢在厚度1/4和厚度中心的局部取向差分布图及定量分析
Fig.8. Local misorientation distribution maps of a quarter of thickness (a) and center of thickness (b), and quantitative analysis of local misorientation in a quarter of thickness and center of thickness (c) (The blue color indicates misorientations less than 1°, green between 1° and 2°, yellow between 2° and 3°, orange between 3° and 4°, and red between 4° and 5°; the high-angle grain boundaries (＞15°) were delineated in black solid lines)