690合金在模拟核电高温高压水中的电化学及原位划伤行为研究
郦晓慧1, 王俭秋2(
), 韩恩厚2, 郭延军1, 郑会3, 杨双亮3
), 韩恩厚2, 郭延军1, 郑会3, 杨双亮3
Electrochemistry and In Situ Scratch Behavior of 690 Alloy in Simulated Nuclear Power High Temperature High Pressure Water
LI Xiaohui1, WANG Jianqiu2(), HAN En-Hou2, GUO Yanjun1, ZHENG Hui3, YANG Shuangliang3
), HAN En-Hou2, GUO Yanjun1, ZHENG Hui3, YANG Shuangliang3
图5. 690合金在空气中单道划伤后划痕底部TiN夹杂物形貌及EDS分析
Fig.5. SEM images (a, c) and EDS result (b) of single scratch bottom around TiN inclusion on alloy 690 in air
(a) cracking at the interface between TiN inclu- sion and substrate
(b) EDS result of point in Fig.5a(c) TiN inclusion fragmented