Hot Deformation Characteristics of Novel Wrought Superalloy GH4975 Extruded Rod Used for 850 ℃ Turbine Disc
ZHANG Yong1(), LI Xinxu1, WEI Kang1, WAN Zhipeng1, JIA Chonglin1, WANG Tao1, LI Zhao1, SUN Yu2, LIANG Hongyan3
), LI Xinxu1, WEI Kang1, WAN Zhipeng1, JIA Chonglin1, WANG Tao1, LI Zhao1, SUN Yu2, LIANG Hongyan3
图8. GH4975合金在不同变形条件下微观组织的TEM像
Fig.8. TEM images of microstructures of GH4975 superalloy deformed at 1150 ℃, 0.001 s-1 (a), 1180 ℃, 0.1 s-1 (c) and 1180 ℃, 1 s-1 (d); Hereinto, Fig.8b is the selected area electron diffraction pattern (SAEDP) of Fig.8a, which is to identify the γ′ precipitates