ODS钢在600和700 ℃静态Pb-Bi共晶中的腐蚀行为及机理
包飞洋1,2, 李艳芬1,2,3(
), 王光全2,4, 张家榕2, 严伟1,2,3, 石全强2,3, 单以银1,2,3, 杨柯1,2, 许斌5, 宋丹戎5, 严明宇5, 魏学栋5
), 王光全2,4, 张家榕2, 严伟1,2,3, 石全强2,3, 单以银1,2,3, 杨柯1,2, 许斌5, 宋丹戎5, 严明宇5, 魏学栋5
Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 ℃
BAO Feiyang1,2, LI Yanfen1,2,3(), WANG Guangquan2,4, ZHANG Jiarong2, YAN Wei1,2,3, SHI Quanqiang2,3, SHAN Yiyin1,2,3, YANG Ke1,2, XU Bin5, SONG Danrong5, YAN Mingyu5, WEI Xuedong5
), WANG Guangquan2,4, ZHANG Jiarong2, YAN Wei1,2,3, SHI Quanqiang2,3, SHAN Yiyin1,2,3, YANG Ke1,2, XU Bin5, SONG Danrong5, YAN Mingyu5, WEI Xuedong5
图5. ODS钢在700 ℃静态LBE中腐蚀不同时间的表面腐蚀形貌
Fig.5. Low and high magnified SEM images of the surface scale formed on ODS steel exposed to static LBE at 700 ℃ for 100 h (a, b) and 500 h (c~f) (Figs.5e and f are high magnified SEM images for the nodular area marked as "e" and flat area marked as "f" in the Fig.5d, respectively)