ODS钢在600和700 ℃静态Pb-Bi共晶中的腐蚀行为及机理
包飞洋1,2, 李艳芬1,2,3(
), 王光全2,4, 张家榕2, 严伟1,2,3, 石全强2,3, 单以银1,2,3, 杨柯1,2, 许斌5, 宋丹戎5, 严明宇5, 魏学栋5
), 王光全2,4, 张家榕2, 严伟1,2,3, 石全强2,3, 单以银1,2,3, 杨柯1,2, 许斌5, 宋丹戎5, 严明宇5, 魏学栋5
Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 ℃
BAO Feiyang1,2, LI Yanfen1,2,3(), WANG Guangquan2,4, ZHANG Jiarong2, YAN Wei1,2,3, SHI Quanqiang2,3, SHAN Yiyin1,2,3, YANG Ke1,2, XU Bin5, SONG Danrong5, YAN Mingyu5, WEI Xuedong5
), WANG Guangquan2,4, ZHANG Jiarong2, YAN Wei1,2,3, SHI Quanqiang2,3, SHAN Yiyin1,2,3, YANG Ke1,2, XU Bin5, SONG Danrong5, YAN Mingyu5, WEI Xuedong5
图4. ODS钢在600 ℃静态LBE中腐蚀100 h的表面形貌
Fig.4. SEM images of surface scale formed on ODS steel after exposed to static LBE at 600 ℃ for 100 h
(a) a representative area (b) regular octahedral particles area marked as "b" in Fig.4a