ODS钢在600和700 ℃静态Pb-Bi共晶中的腐蚀行为及机理
包飞洋1,2, 李艳芬1,2,3(
), 王光全2,4, 张家榕2, 严伟1,2,3, 石全强2,3, 单以银1,2,3, 杨柯1,2, 许斌5, 宋丹戎5, 严明宇5, 魏学栋5
), 王光全2,4, 张家榕2, 严伟1,2,3, 石全强2,3, 单以银1,2,3, 杨柯1,2, 许斌5, 宋丹戎5, 严明宇5, 魏学栋5
Corrosion Behaviors and Mechanisms of ODS Steel Exposed to Static Pb-Bi Eutectic at 600 and 700 ℃
BAO Feiyang1,2, LI Yanfen1,2,3(), WANG Guangquan2,4, ZHANG Jiarong2, YAN Wei1,2,3, SHI Quanqiang2,3, SHAN Yiyin1,2,3, YANG Ke1,2, XU Bin5, SONG Danrong5, YAN Mingyu5, WEI Xuedong5
), WANG Guangquan2,4, ZHANG Jiarong2, YAN Wei1,2,3, SHI Quanqiang2,3, SHAN Yiyin1,2,3, YANG Ke1,2, XU Bin5, SONG Danrong5, YAN Mingyu5, WEI Xuedong5
图1. 腐蚀实验设备的结构示意图
Fig.1. Schematic of corrosion test equipment (LBE—lead-bismuth eutectic)