15CrMoG钢包晶凝固特征与机制
李亚强1, 刘建华1(
), 邓振强1, 仇圣桃2, 张佩3, 郑桂芸3
), 邓振强1, 仇圣桃2, 张佩3, 郑桂芸3
Peritectic Solidification Characteristics and Mechanism of 15CrMoG Steel
LI Yaqiang1, LIU Jianhua1(), DENG Zhenqiang1, QIU Shengtao2, ZHANG Pei3, ZHENG Guiyun3
), DENG Zhenqiang1, QIU Shengtao2, ZHANG Pei3, ZHENG Guiyun3
图2. 冷却速率为5 ℃/min 时δ相析出和包晶相变原位观察
Fig.2. In situ observations of δ precipitation and peritectic phase transformation at a cooling rate of 5 ℃/min (L—liquid phase)
(a, b) precipitation and growth of δ-ferrite (c, d) peritectic reaction (e, f) peritectic transformation