基于有限元分析的准晶磨料强化不锈钢表面钝化行为
陈永君1,2, 白妍1, 董闯2,3(
), 解志文1, 燕峰1, 吴迪1
), 解志文1, 燕峰1, 吴迪1
Passivation Behavior on the Surface of Stainless Steel Reinforced by Quasicrystal-Abrasive via Finite Element Simulation
CHEN Yongjun1,2, BAI Yan1, DONG Chuang2,3(), XIE Zhiwen1, YAN Feng1, WU Di1
), XIE Zhiwen1, YAN Feng1, WU Di1
图10. 304不锈钢经不同磨料处理钝化后在3.5%NaCl溶液中浸泡24 h形成钝化膜的Mott-Schottky曲线
Fig.10. Mott-Schottky plots of the oxide films formed on 304 stainless steel polished by three kinds of abrasives in neutrally aerated 3.5%NaCl solution with the immersion time of 24 h (Csc—capacitance of space charge layer )