羟基亚乙基二膦酸对20SiMn钢在含Cl-混凝土模拟孔隙液中的缓蚀行为
曹凤婷1,2, 魏洁1, 董俊华1(
), 柯伟1, 王铁钢2, 范其香2
), 柯伟1, 王铁钢2, 范其香2
Corrosion Inhibition Behavior of 1-Hydroxyethylidene-1, 1-Diphosphonic Acid on 20SiMn Steel in Simulated Concrete Pore Solution Containing Cl-
CAO Fengting1,2, WEI Jie1, DONG Junhua1(), KE Wei1, WANG Tiegang2, FAN Qixiang2
), KE Wei1, WANG Tiegang2, FAN Qixiang2
图10. 20SiMn钢在1 mol/L NaCl饱和Ca(OH)2空白或添加1.441×10-4 mol/L HEDP溶液中浸泡1 h的XPS分峰处理结果
Fig.10. Deconvoluted XPS spectra of Cl2p (a), P2p (b), Fe2p (c) and O1s (d) of 20SiMn steel immersed for 1 h in 1 mol/L NaCl saturated Ca(OH)2 solution without and with 1.441×10-4 mol/L HEDP