Post-Dynamic Softening of Austenite in a Ni-30%Fe Model Alloy After Hot Deformation

CHEN Wenxiong¹^,², HU Baojia¹^,², JIA Chunni¹^,², ZHENG Chengwu¹^,²(

), LI Dianzhong¹^,²

图6. Ni-30%Fe 合金在T=900 ℃、 $ε ˙$ =0.001 s^-1 条件下变形至应变ε=0.3后续保温不同时间过程中微观组织演变的EBSD像

Fig.6. EBSD maps of the Ni-30%Fe alloy at different annealing time of 0 s (a), 2 s (b), 10 s (c) and 60 s (d) after the hot deformation under T=900 ℃ and $ε ˙$ =0.001 s^-1 at a strain of 0.3 (The silver, green, blue, black and red lines represent boundaries with 0.8°≤θ<2°, 2°≤θ<5°, 5°≤θ<15°, θ≥15° and ?3 twin boundaries, respectively)