热浸镀锌高强汽车板界面组织对其拉伸断裂行为的影响
于家英1, 王华1, 郑伟森1, 何燕霖1(
), 吴玉瑞2, 李麟1
), 吴玉瑞2, 李麟1
Effect of the Interface Microstructure of Hot-Dip Galvanizing High-Strength Automobile Steel on Its Tensile Fracture Behaviors
YU Jiaying1, WANG Hua1, ZHENG Weisen1, HE Yanlin1(), WU Yurui2, LI Lin1
), WU Yurui2, LI Lin1
图2. 3种高强钢经HCl、H2SO4腐蚀后的表面形貌及EDS分析
Fig.2. SEM images and EDS analyses of the inhibition layer in steels No.1 (a), No.2 (b) and No.3 (c) corroded by hydrochloric acid, and steel No.2 corroded by sulphuric acid (d)