Mechanical Properties of AlSiMg Alloy Specifically Designed for Selective Laser Melting
GENG Yaoxiang(), FAN Shimin, JIAN Jianglin, XU Shu, ZHANG Zhijie, JU Hongbo, YU Lihua, XU Junhua
), FAN Shimin, JIAN Jianglin, XU Shu, ZHANG Zhijie, JU Hongbo, YU Lihua, XU Junhua
图9. SLM成形AlSiMg1.5样品在150 ℃下时效处理18和48 h后显微组织的SEM像
Fig.9. SEM images of SLM-formed AlSiMg1.5 samples after ageing at 150 ℃ for 18 h (a) and 48 h (b)