Progress in Research on the Alloying of Binary Immiscible Metals

HUANG Yuan, DU Jinlong, WANG Zumin

表1 Mo/Ag双层金属在不同温度下合金化相同时间后的VEPAS测试S参数峰值和峰值相应深度[101]

Table 1 S parameter values and corresponding depth of the S peak for the Mo/Ag laminated samples annealed at different temperatures[101]

Annealing temperature / ℃ S parameter value of S peak Depth / nm 300 0.4635 155 400 0.4657 119 500 0.4622 119 600 0.4604 108 700 0.4501 78