高温合金盘锻件制备过程残余应力的演化规律及机制
毕中南1,2(
),秦海龙1,2,董志国3,王相平3,王鸣3,刘永泉3,杜金辉1,2,张继1,2
),秦海龙1,2,董志国3,王相平3,王鸣3,刘永泉3,杜金辉1,2,张继1,2
Residual Stress Evolution and Its Mechanism During the Manufacture of Superalloy Disk Forgings
BI Zhongnan1,2(),QIN Hailong1,2,DONG Zhiguo3,WANG Xiangping3,WANG Ming3,LIU Yongquan3,DU Jinhui1,2,ZHANG Ji1,2
),QIN Hailong1,2,DONG Zhiguo3,WANG Xiangping3,WANG Ming3,LIU Yongquan3,DU Jinhui1,2,ZHANG Ji1,2
图16. GH4169合金盘锻件加工前后尺寸和残余应力测试点
Fig.16. Schematics of machining process for GH4169 alloy disk forging(a, b) dimensions of disk before and after machining, respectively (unit: mm) (c) schematic of the disks after machining d, e) residual stress measuring locations of disk before and after machining, respectively (unit: mm)