我国典型金属间化合物基高温结构材料的研究进展与应用
宫声凯1(
),尚勇1,张继2,郭喜平3,林均品4,赵希宏5
),尚勇1,张继2,郭喜平3,林均品4,赵希宏5
Application and Research of Typical Intermetallics-Based High Temperature Structural Materials in China
GONG Shengkai1(),SHANG Yong1,ZHANG Ji2,GUO Xiping3,LIN Junpin4,ZHAO Xihong5
),SHANG Yong1,ZHANG Ji2,GUO Xiping3,LIN Junpin4,ZHAO Xihong5
图5. IC21合金的1100 ℃循环氧化增重曲线及[111]取向的1100 ℃、137 MPa蠕变曲线
Fig.5. Cyclic oxidation weight gain curves of IC21 at 1100 ℃ (a) and the creep curve of IC21[111] at 1100 ℃ under 137 MPa (Insets show the morpholoyies of alloys at different time) (b)