一种第二代镍基单晶高温合金1150 ℃原位拉伸断裂机制研究
|
马晋遥 1,王晋 1,赵云松 3,张剑 3,张跃飞 1( ),李吉学 2,张泽 2
|
Investigation of In Situ 1150 ℃ High Temperature Deformation Behavior and Fracture Mechanism of a Second Generation Single Crystal Superalloy
|
Jinyao MA 1,Jin WANG 1,Yunsong ZHAO 3,Jian ZHANG 3,Yuefei ZHANG 1( ),Jixue LI 2,Ze ZHANG 2
|
|
图7. 镍基单晶高温合金1150 ℃原位拉伸过程中不同载荷状态下样品形变过程
|
Fig.7. In situ observation of micro hole initiation and sample deformation process under different loading conditions |
|
|
|
|