一种第二代镍基单晶高温合金1150 ℃原位拉伸断裂机制研究
马晋遥1,王晋1,赵云松3,张剑3,张跃飞1(
),李吉学2,张泽2
),李吉学2,张泽2
Investigation of In Situ 1150 ℃ High Temperature Deformation Behavior and Fracture Mechanism of a Second Generation Single Crystal Superalloy
Jinyao MA1,Jin WANG1,Yunsong ZHAO3,Jian ZHANG3,Yuefei ZHANG1(),Jixue LI2,Ze ZHANG2
),Jixue LI2,Ze ZHANG2
图2. 加热拉伸实验平台与SEM联用照片及加热拉伸平台结构示意图
Fig.2. Heating and tensile platform combined with SEM (a) and schematic of heating tensile stage (b)