一种第二代镍基单晶高温合金1150 ℃原位拉伸断裂机制研究
马晋遥1,王晋1,赵云松3,张剑3,张跃飞1(
),李吉学2,张泽2
),李吉学2,张泽2
Investigation of In Situ 1150 ℃ High Temperature Deformation Behavior and Fracture Mechanism of a Second Generation Single Crystal Superalloy
Jinyao MA1,Jin WANG1,Yunsong ZHAO3,Jian ZHANG3,Yuefei ZHANG1(),Jixue LI2,Ze ZHANG2
),Jixue LI2,Ze ZHANG2
图1. 原位加热拉伸试样尺寸
Fig.1. Dimension of in situ SEM heating tensile specimen (unit: mm)