基于中间过渡层的 5A06/0Cr18Ni10Ti 气化冲击焊接工艺研究
陈树君
Study on Vaporizing Foil Actuator Welding Process of 5A06/0Cr18Ni10Ti with Interlayer
Shan SU
表1
材料化学成分
Table 1
Chemical compositions of workpieces
Material
Si
Fe
Cu
Mn
Mg
Zn
Ti
Ni
C
Cr
N
Al
5A06
0.40
0.4
0.1
0.5~0.8
5.8~6.8
0.2
0.1
-
-
-
-
Bal.
3003
0.60
0.7
0.05~0.20
1.0~1.5
-
0.1
-
-
-
-
-
Bal.
0Cr18Ni10Ti
0.75
Bal.
-
2.0
-
-
0.7
9~12
0.08
17~19
0.1
-