交叉轧制周期对高纯Ta板变形及再结晶梯度的影响
|
祝佳林,刘施峰,曹宇,柳亚辉,邓超,刘庆
|
Effect of Cross Rolling Cycle on the Deformed and Recrystallized Gradient in High-Purity Tantalum Plate
|
Jialin ZHU,Shifeng LIU,Yu CAO,Yahui LIU,Chao DENG,Qing LIU
|
|
表2 不同厚度层不同取向晶粒内的储存能及用于计算的相关参数 |
Table 2 Orientation-dependent stored energy of 1 and 2 cycle samples at different thicknesses by XLPA |
|
Rolling cycle | Position | Diffraction plane | Yhkl[21,22,23] | vhkl[21,22,23] | Br | Ba | Ehkl |
---|
| | | GPa | | | | J·mol-1 | First cycle | Surface | (200) | 145.517 | 0.316 | 0.185 | 0.100 | 3.997 | | | (222) | 387.931 | 0.362 | 0.318 | 0.140 | 5.037 | | Quarter | (200) | 145.517 | 0.316 | 0.179 | 0.100 | 3.636 | | | (222) | 387.931 | 0.362 | 0.302 | 0.140 | 4.425 | | Center | (200) | 145.517 | 0.316 | 0.218 | 0.100 | 6.192 | | | (222) | 387.931 | 0.362 | 0.453 | 0.140 | 11.469 | Second cycle | Surface | (200) | 145.517 | 0.316 | 0.190 | 0.100 | 4.306 | | | (222) | 387.931 | 0.362 | 0.312 | 0.140 | 4.804 | | Quarter | (200) | 145.517 | 0.316 | 0.186 | 0.100 | 4.058 | | | (222) | 387.931 | 0.362 | 0.295 | 0.140 | 4.166 | | Center | (200) | 145.517 | 0.316 | 0.197 | 0.100 | 4.753 | | | (222) | 387.931 | 0.362 | 0.326 | 0.140 | 5.356 |
|
|
|